All-in-one bio-derived poly(L-lactic acid)-based composite with fire-resistance and smoke-suppression performance

The flammability of bio-derived poly(L-lactic acid) (PLA) greatly limits its application and eco-friendly multifunctional fire-fighting PLA-based composites are highly desired. In this work, a fully bio-based modified CS (C-CS) and commercially available eco-friendly ammonium polyphosphate (APP) were used as a synergistic flame retardant agent (C-CS/APP) to investigate its effects on fire-proofing performance and diverse properties of the PLA. The PLA/5%C-CS/5%APP composite exhibited excellent fire-resistant performance with anti-droplet, smoke-suppression and self-extinguishing property, and its limited oxygen index enhanced by 37 % (compared with neat PLA). This composite reached the highest V-0 fire safety rating, and its peak of heat release rate and total smoke production reduced by 26.5 % and 68.3 %, respectively. In addition, the char residue yield after the cone calorimeter test increased by 46 times in the composite, indicating an outstanding char-forming capacity. The condensed phase flame retardancy played a crucial role on the fire-fighting of this composite, that is, significantly enhanced char residue (as a physical barrier) blocked the heat exchange and O₂ entry, and further suppressed the combustion reaction. Additionally, the PLA-based composite showed outstanding UV-absorption property, good anti-bacterial effect, and increased hydrophilicity and crystallizability.