Comparative Evaluation of Dental Enamel Microhardness Following Various Methods of Interproximal Reduction: A Vickers...

Interproximal enamel reduction, also known as stripping, is a common orthodontic procedure that reduces the mesiodistal diameter of teeth, allowing for a balance of available space in dental arches. The aim of this study was to assess the enamel surface microhardness resulting from the application of currently available methods for interproximal reduction. Forty-two extracted human permanent teeth were divided into six different groups, each subjected to a therapeutic stripping procedure using various methods (i.e., diamond burs, abrasive strips of 90 μm, 60 μm, 40 μm, and 15 μm, and abrasive discs). Stripping was performed by a single individual in accordance with the manufacturers' recommendations for the various systems used. One of the proximal faces of the tooth underwent IPR, while the other side remained untreated for control. The hardness of the enamel surface was measured using a Vickers hardness tester. The control group achieved the hardest enamel surface (354.4 ± 41.02 HV1), while the lowest was observed for enamel surfaces treated with 90 µm abrasive strips (213.7 ± 118.6). The only statistically significant difference was identified in comparisons between the values measured for the control group and those obtained after stripping with diamond burs (p = 0.0159). Enamel microhardness varied depending on the stripping instrument used, but no statistically significant differences were found (p > 0.05). Optimal microhardness values, close to those of healthy enamel, were achieved after mechanical treatment with 15 µm abrasive strips and abrasive discs. Dental stripping is a safe therapeutic procedure that has a relatively minor influence on the microhardness of surface enamel.