The Influence of Slag Content on the Structure and Properties of the Interfacial Transition Zone of Ceramisite...

Ceramisite lightweight concrete has excellent performance and relatively light self-weight characteristics. At the same time, the recent development of green high-performance concrete and prefabricated components has also brought the abundant utilization of these mineral mixture. An interfacial transition zone exists between the hardened cement paste and the aggregate, which is the weakest part of the concrete, characterized by high porosity and low strength. In order to study the effect of slag content on the interfacial transition zone in lightweight high-strength concrete, experiments were designed to replace cement with slag at different contents (0%, 5%, 10%, 15%). A series of studies was conducted on its macro-strength, microstructure, and composition. The results indicated that the addition of slag improved the porosity and width of the interfacial transition zone. Adding slag did not reduce the thickness of the concrete interfacial transition zone significantly at 3 d, but it led to significant improvement in the thickness of the interfacial transition zone at 28 d, and the thickness of the interfacial zone at 28 d was reduced from 19 μm to 8.5 μm, a reduction of 55%. The minimum value of microhardness in the slurry region of the interfacial specimens also increased from 19 MPa to 26 MPa, an increase of 36%. In addition, the structural density of the interfacial region was further increased, resulting in varying degrees of improvement in the macroscopic anti-splitting strength. One of the important reasons for this phenomenon is that the addition of slag optimizes the chemical composition of the interface and promotes the continuation of the pozzolanic reactivity, which further enhances the hydration at the interface edge.