Effects of Different Oxidation Methods on the Wetting and Diffusion Characteristics of a High-Alumina Glass Sealant...

Glass-to-metal seals are a very important element in the construction of vacuum tubes, electric discharge tubes, pressure-tight glass windows in metal cases, and metal or ceramic packages of electronic components. This paper presents the influence of different pretreatment methods on the high-temperature wettability of 304 stainless steel by high-alumina glass sealing. The pretreatment of the steel included laser surface melting and pre-oxidizing. The bonding characteristics of glass and stainless steel directly depend on the wettability in terms of the measured wetting angle, the type of oxide formed at the stainless steel surface, and the microstructural changes during the manufacturing process. The oxide film thickness on the stainless steel surface was evaluated to determine the optimal parameters. The film was wetted with high-alumina glass powder at different temperatures. The results showed that pre-oxidation decreased the wetting angle from 56.2° to 33.6°, while for the laser-melted surface, the wetting angle decreased from 49.8° to 31.5°. Scanning electron microscopy (SEM) revealed that the oxide film on the laser-melted surface was thicker and denser than that formed on the pre-oxidized surface. The present work shows that laser surface melting has a greater beneficial influence on the wetting and diffusion characteristics of 304 stainless steel sealed by high-alumina glass.