Microstructure and Hardness Characteristics of Swing-Arc SAW Hardfacing Layers

Hot-rolled backup rolls are widely used in steel rolling and usually need to be repaired by arc hardfacing after becoming worn. However, a corrugated-groove defect commonly occurs on the roll surface due to the uneven hardness distribution in the hardfacing layers, affecting the proper usage of the roll. Accordingly, a new swing-arc submerged arc welding (SA-SAW) process is proposed to attempt to solve this drawback. The microstructure and hardness are then investigated experimentally for both SAW and SA-SAW hardfacing layers. It is revealed that a self-tempering effect occurs in the welding pass bottom and the welding pass side neighboring the former pass for both processes, refining the grain in the two areas. In all the zones, including the self-tempering zone (STZ), heat-affected zone (HAZ), and not-heat-affected zone in the welding pass, both SAW and SA-SAW passes crystallize in a type of columnar grain, where the grains are the finest in STZ and the coarsest in HAZ. In addition, the arc swing improves the microstructure homogeneity of the hardfacing layers by obviously lowering the tempering degree in HAZ while promoting the even distribution of the arc heat. Accordingly, the hardness of the SA-SAW bead overall increases and distributes more uniformly with a maximum difference of < 80 HV_0.5 along the horizontal direction of the bead. This hardness difference in SA-SAW is accordingly decreased by ~38.5% compared to that of the SAW bead, further indicating the practicability of the new process.