The Microstructure and Mechanical Properties of Si₃N_4f/BN/SiBCN Microcomposites Fabricated by the PIP Process

SiBCN ceramics based on SiC, BN and Si₃N₄ structures have good comprehensive properties such as high-temperature resistance, oxidation resistance, creep resistance and long life, which makes it one of the very promising ceramic material systems in military and aerospace fields, etc. In this study, SiBCN ceramics, as well as Si₃N_4f/BN/SiBCN microcomposites, were prepared by a polymer infiltration pyrolysis method using PBSZ as the polymer precursor. The PBSZ was completely ceramized by pyrolysis at 900 °C. The weight loss and elemental bonding forms of the products after the pyrolysis of the precursors hardly changed from 600 °C to 900 °C. After pyrolysis at 600 °C for 4 h and using the BN coating obtained from twice deposition as the interfacial phase, a more desirable weak interface of fiber/matrix with a binding strength of 21.96 ± 2.01 MPa can be obtained. Si₃N_4f/BN/SiBCN ceramic matrix microcomposites prepared under the same pyrolysis conditions have a relatively good tensile strength of 111.10 MPa while retaining a weak interface between the fibers and the matrix. The results of the study provide more theoretical and methodological support for the application of new composite structural ceramic material systems.