Optical properties of monolithic zirconia fabricated with nanoparticle jetting
Zhiyao Zhu1, Xinyue Huang2, Jizhe Lyu2
1Graduate student, Department of Prosthodontics, Peking University School and Hospital of Stomatology & National Center for Stomatology & National Clinical Research Center for Oral Diseases & National Engineering Research Center of Oral Biomaterials and Digital Medical Devices, Beijing, PR China.
Statement Of Problem:
Excellent optical properties are essential for esthetic dental materials. However, the translucency and color masking ability of zirconia fabricated with nanoparticle jetting (NPJ), a type of printed zirconia, are unknown.
Purpose:
The purpose of this in vitro study was to evaluate the translucency and color masking ability of zirconia fabricated using NPJ.
Material And Methods:
A total of 90 specimens with thicknesses of 1.5, 1.0, and 0.5 mm were fabricated using high translucent milled zirconia (HT), low translucent milled zirconia (LT), and NPJ. CIELab values (L*, a*, and b*) of the specimens over 7 backgrounds, black, white, VitaB1, VitaA2, VitaA4, gold alloy (Au), and titanium (Ti), were obtained using a spectral radiometer. The relative translucency parameter (RTP) and color difference (∆E) of specimens over VitaB1, VitaA4, Au, and Ti were determined using VitaA2 as the control with the CIEDE2000 color difference equation. The normality of the data distribution was determined using the Shapiro-Wilk test. Differences among groups were analyzed using 2-way analysis of variance and the Student-Newman-Keuls (SNK) post hoc test (α=.05). The ∆E of specimens was analyzed according to perceptibility (∆E=0.8) and acceptability (∆E=1.8) thresholds using the 1 sample t test. The correlation between RTP and ∆E and RTP/∆E and thickness was examined using the Pearson correlation analysis.
Results:
Statistically significant differences were observed in translucency and color masking ability among HT, LT, and NPJ (P<.05). The RTP value was the lowest for zirconia fabricated with NPJ (P<.001) and highest for HT (P<.001). Monolithic zirconia fabricated with NPJ had lower ∆E values than those of HT and LT for the same thickness and background (P<.05). A positive correlation was found in RTP and ∆E (P<.001). A negative correlation was observed in RTP and thickness (P<.001) and ∆E and thickness across a constant background (P<.001).
Conclusions:
Zirconia fabricated with NPJ was less translucent and had a greater color masking ability for discolored backgrounds than HT and LT.