Leaching and cytotoxicity of bismuth oxide in ProRoot MTA - A laboratory investigation

The present study examined the leaching and cytotoxicity of bismuth from ProRoot MTA and aimed to identify whether bismuth leaching was affected by the cement base and the immersion regime used.

The leaching profile of bismuth was examined from ProRoot MTA and compared with hydroxyapatite containing 20% bismuth oxide as well as hydroxyapatite and tricalcium silicate to investigate whether bismuth release changed depending on the cement base. Bismuth leaching was determined after 30 and 180 days of ageing immersed in Dulbecco's modified Eagle's medium (DMEM) using mass spectroscopy (ICP-MS). The media were either unchanged or regularly replenished. The pH, surface microstructure and phase changes of aged materials were assessed. Wistar rat femoral bone marrow stromal cells (BMSCs) and cutaneous fibroblasts were isolated, cultured and seeded for cell counting (trypan blue live/dead) after exposure to non-aged, 30- and 180-days-aged samples in regularly replenished DMEM. Aged DMEM in contact with materials was also used to culture BMSCs to investigate the effect of material leachates on the cells. Gene expression analysis was also carried out after direct exposure of cells to non-aged materials. Differences between groups were statistically tested at a significance level of 5%.

All materials exhibited alterations after immersion in DMEM and this increased with longer exposure times. The bismuth leached from ProRoot MTA as detected by ICP-MS. Aged ProRoot MTA samples exhibited a black discolouration and surface calcium carbonate deposition. ProRoot MTA influenced cell counts after direct exposure and its 180-days leachates reduced BMSC viability. After direct BMSC contact with non-aged ProRoot MTA an upregulation of metallothionein (MT1 and MT2A) expression and down-regulation of collagen-1a (Col-1a) and bone sialoprotein (BSP) expression was identified.

Bismuth leaching was observed throughout 180-days observation period from all materials containing bismuth oxide. This negatively influenced cell viability and gene expression associated with bismuth exposure. This is the first study to report that metallothionein gene expression was influenced by exposure to ProRoot MTA.