Constructing An Oxyhalide Interface for 4.8 V-Tolerant High-Nickel Cathodes in All-Solid-State Lithium-Ion Batteries

All-solid-state lithium batteries (ASSBs) have received increasing attentions as one promising candidate for the next-generation energy storage devices. Among various solid electrolytes, sulfide-based ASSBs combined with layered oxide cathodes have emerged due to the high energy density and safety performance, even at high-voltage conditions. However, the interface compatibility issues remain to be solved at the interface between the oxide cathode and sulfide electrolyte. To circumvent this issue, we propose a simple but effective approach to magic the adverse surface alkali into a uniform oxyhalide coating on LiNi_0.8Co_0.1Mn_0.1O₂ (NCM811) via a controllable gas-solid reaction. Due to the enhancement of the close contact at interface, the ASSBs exhibit improved kinetic performance across a broad temperature range, especially at the freezing point. Besides, owing to the high-voltage tolerance of the protective layer, ASSBs demonstrate excellent cyclic stability under high cutoff voltages (500 cycles~94.0 % at 4.5 V, 200 cycles~80.4 % at 4.8 V). This work provides insights into using a high voltage stable oxyhalide coating strategy to enhance the development of high energy density ASSBs.