Nondestructive Direct Patterning of Both Hole Transport and Emissive Layers for Pixelated Quantum-Dot Light-Emitting...

Considering the increasing demand for high-resolution light-emitting diodes (LEDs), it is important that direct fine patterning technologies for LEDs be developed, especially for quantum-dot LEDs (QLEDs). Traditionally, the patterning of QLEDs relies on resin-based photolithography techniques, requiring multiple steps and causing performance deterioration. Nondestructive direct patterning may provide an easy and stepwise method to achieve fine-pixelated units in QLEDs. In this study, two isomeric tridentate cross-linkers (X8/X9) are presented and can be blended into the hole transport layer (HTL) and the emissive layer (EML) of QLEDs. Because of their photosensitivity, the in situ cross-linking process can be efficiently triggered by ultraviolet irradiation, affording high solvent resistance and nondestructive direct patterning of the layers. Red QLEDs using the cross-linked HTL demonstrate an impressive external quantum efficiency of up to 22.45%. Through lithographic patterning enabled by X9, line patterns of HTL and EML films exhibit widths as narrow as 2 and 4 μm, respectively. Leveraging the patterned HTL and EML, we show the successful fabrication of pixelated QLED devices with an area size of 3 × 3 mm², alongside the successful production of dual-color pixelated QLED devices. These findings showcase the promising potential of direct patterning facilitated by engineered cross-linkers for the cost-effective fabrication of pixelated QLED displays.