Metal Ion-Induced Acid Hydrolysis Strategy for the One-Step Synthesis of Tough and Highly Transparent Hydrolyzed...

Polyacrylamide (PAM) hydrogel is hard to enhance through coordination bonds because amide groups rarely coordinate with metal ions strongly in an aqueous solution. It is known that the aqueous solution of ZrOCl₂.8H₂O can be strongly acidic depending on its concentration. Consequently, through a facile one-step metal ion-induced acid hydrolysis strategy (MIAHS), tough and highly transparent hydrolyzed PAM physical hydrogels are prepared by using ZrOCl₂.8H₂O in this work. The formation of the partially hydrolyzed PAM physical hydrogels elucidates that the side reaction of imidization during common acid hydrolysis of PAM can be perfectly overcome because the structure of the Zr(IV) ion and its interaction with amide groups promote selective acidic hydrolysis from amide to carboxyl groups. Compared to most coordination cross-linked hydrogels, which need at least two-step fabrication, the hydrolyzed PAM hydrogel via MIAHS can be obtained by one-step synthesis due to the weak interaction between amide groups and Zr(IV). The obtained PAM hydrogel cross-linked by hydrogen bonds and coordination bond between Zr(IV) and carboxyl is a multibond network (MBN) and can achieve hierarchical energy dissipation, which exhibits excellent mechanical properties (tensile strength of 3.15 MPa, elongation at break of 890%, and toughness of 17.0 MJ m^-3), high transparence (transmittance of 95%), and outstanding conductivity (5.6 S m^-1) at water content of 80 wt %. The high gauge factor (from 2.24 to 12.8 as the strain increases from 0 to 400%) endows the hydrolyzed PAM hydrogels with promising application as strain sensors. Furthermore, in addition to ZrOCl₂.8H₂O, the fact that various hydrolyzable compounds of Ti(IV), Zr(IV) Hf(IV), and Sn(IV) can also fabricate tough hydrolyzed PAM hydrogels verifies the universality of MIAHS. Therefore, the simple, efficient, and universal MIAHS will shed new light on preparing functional PAM-based hydrogels.