Biophysical studies of modified PVC sheet based on sunflower oil for antistatic and blood bags applications

In this work, the surface of polyvinyl chloride PVC sheet was modified by blending it with sunflower seed oil SSO to obtain PVC sheet/SSO films of ratios 100/0, 90/10, 80/20, 70/30, 60/40, and 50/50 (v/v)% using the solution casting method. Various techniques were used to characterize the prepared films, besides the use of hemolysis assays and blood clot formation tests. FTIR spectra revealed that there was a good interaction between the PVC sheet and the oil. The dielectric measurement indicated that SSO addition enhanced the dielectric properties of the sheet. The study of dielectric relaxation times confirmed the interaction between SSO and the sheet. DC conductivity increased to 6 × 10^-6 S/m, so it could be applied in antistatic applications. Also, SSO addition increased the value of the thermal stability. According to SEM micrographs, the film was roughened at a ratio of 60/40 and smoothed out at 50/50. This behavior was confirmed with roughness and contact angle measurement results, in which the film of ratio 60/40 had the highest value equal to (72.03°) and then decreased at 50/50 to (59.62°). These results were confirmed by XRD measurement as the crystallinity increased at the film ratio of 60/40 and decreased again at 50/50. Also, the ratio of 60/40 demonstrated a large decrease in thrombus weights along with a slight increase in hemolysis, which is within the acceptable range and has a high degree of biocompatibility, so this concentration is recommended to be used in blood bags applications.