Pd@CuInP2S6 Core-Shell Nanospheres with Exceptional Hydrogen Evolution Capability and Stability in Both Alkaline and
Guoshuai Fu1, Kangfan Xie1, Bo Yan1
1State Key Laboratory of Optoelectronic Materials and Technologies, Nanotechnology Research Center, Guangzhou Key Laboratory of Flexible Electronic Materials and Wearable Devices, School of Materials Science & Engineering, Sun Yat-sen University, Guangzhou, Guangdong, 510275, P. R. China.
Abstract:
By combining Pd with 2D layered crystal CuInP2S6 (CIPS) via laser irradiation in liquids, low-loading Pd@CIPS core-shell nanospheres are fabricated as an efficient and robust electrocatalysts for HER in both alkaline and acidic media under large current density (⩾1000 mA cm-2). Pd@CIPS core-shell nanosphere has two structural features, i) the out-shell is the nanocomposite of PdHx and PdInHx, and ii) there is a kind of dendritic structure on the surface of nanospheres, while the dendritic structure porvides good gas desorption pathway and cause the Pd@CIPS system to maintain higher HER activity and stability than that of commercial Pt/C under large current densities. Pd@CIPS exhibits very low overpotentials of -218 and -313 mV for the large current density of 1000 mA cm-2, and has a small Tafel slope of 29 and 63 mV dec-1 in 0.5 m H2SO4 and 1 m KOH condition, respectively. Meanwhile, Pd@CIPS has an excellent stability under -10 and -500 mA cm-2 current densities and 50 000 cycles cyclic voltammetry tests in 0.5 m H2SO4 and 1 m KOH, respectively, which being much superior to that of commercial Pt/C. Density functional theory (DFT) reveals that engineering electronic structure of PdHx and PdInHx nanostructure can strongly weaken the Pd─H bonding.