Formulation and Characterization of Triamcinolone Acetonide Acetate-Loaded Microspheres Prepared by a Static Mixing
Huan-Huan Du1,2, Li-Rong Wang1, Xin-Hong Wu1
1College of Pharmaceutical Sciences, Soochow University, Suzhou, People's Republic of China.
Purpose:
Reproducibility and scale-up production of microspheres through spray drying present significant challenges. In this study, biodegradable microspheres of Triamcinolone Acetonide Acetate (TAA) were prepared using a novel static mixing method by employing poly( lactic-co-glycolic acid) (PLGA) as the sustained-release carrier.
Methods:
TAA-loaded microspheres (TAA-MSs) were prepared using a static mixing technique. The PLGA concentration, polyvinyl alcohol concentration (PVA), phase ratio of oil/water, and phase ratio of water/solidification were optimized in terms of the particle size, drug loading (DL), and encapsulation efficiency (EE) of TAA-MSs. The morphology of TAA-MSs was examined using Scanning Electron Microscopy (SEM), while the physicochemical properties were evaluated through X-ray diffraction (XRD), Differential Scanning Calorimetry (DSC), and Fourier Transform Infrared Spectroscopy (FT-IR). The in vitro release of TAA-MSs was compared to that of the pure drug (TAA) using a water-bath vibration method in the medium of pH 7.4 at 37°C.
Results:
The formulation composition and preparation condition for the preparation of TAA-MSs were optimized as follows: the PLGA concentration was 1%, the phase ratio of oil(dichloromethane) /water (PVA solution) was 1:3, the phase ratio of water (PVA solution)/solidification was 1:2. The optimized TAA-MSs displayed spherical particles with a size range of 30-70 μm, and DL and EE values of 27.09% and 98.67%, respectively. Moreover, the drug-loaded microspheres exhibited a significant, sustained release, with 20% of the drug released over a period of 28 days. The XRD result indicated that the crystalline form of TAA in microspheres had been partly converted into the amorphous form. DSC and FT-IR results revealed that some interactions between TAA and PLGA occurred, indicating that the drug was effectively encapsulated into PLGA microspheres.
Conclusion:
TAA-loaded PLGA microspheres have been successfully prepared via the static mixing technique with enhanced EE and sustained-release manner.