A High-Mobility n-Type Noncovalently-Fused-Ring Polymer for High-Performance Organic Thermoelectrics

Conjugated polymers are emerging as competitive candidates for organic thermoelectrics (OTEs). However, to make the device truly pervasive, both p- and n-type conjugated polymers are essential. Despite great efforts, no n-type equivalents to the p-type benchmark PEDOT:PSS exist to date mainly due to the low electrical conductivity (σ). Herein, a near-amorphous n-type conjugated polymer, namely pDFSe, is reported with high σ by achieving the synergy between charge transport and doping efficiency. The polymer pDFSe is synthesized based on an acceptor-triad moiety of diketopyrrolopyrrole-difluorobenzoselenadiazole-diketopyrrolopyrrole (DFSe), which has the noncovalently-fused-ring structure to reinforce the backbone rigidity. Furthermore, an axisymmetric thiophene-selenophene-thiophene donor is introduced, which enables the formation of near-amorphous microstructures. The above merits ensure good doping efficiency without scarifying efficient intrachain charge-carrier transport. Thus, pDFSe-based n-type transistors exhibit high electron mobility up to 6.15 cm² V^-1 s^-1, much higher than its reference polymer pDSe without the noncovalently-fused-ring structure (0.77 cm² V^-1 s^-1). Further upon n-doping, pDFSe demonstrates excellent σ of 62.6 S cm^-1 and maximum power factor of 133.1 μW m^-1 K^-2, which are among the highest values reported for solution-processed n-type polymers. The results demonstrate the great potential of near-amorphous n-type conjugated polymers with noncovalently-fused-ring structure for the next-generation OTEs.