Fully upgrade bamboo biomass into three multifunctional products through biphasic γ-valerolactone and aqueous...

In this manuscript, three components of lignocellulosic biomass were obtained by deconstructing bamboo with γ-valerolactone-H₂O biphasic system, and the delignification rate of 80.92 % was achieved at 120 °C for 90 min. Lignin nanospheres with diameters ranging from 75 nm to 2 um could be customized by varying the self-assembly rate. Furthermore, the lignin nanospheres-poly(vinyl alcohol) film was prepared by cross-linking lignin nanospheres and poly(vinyl alcohol), which can obtain 90 % ultraviolet absorption capacity, while the light transmittance in non-ultraviolet band was almost unchanged. At the same time, due to the strong hydrogen formation between lignin nanospheres and poly(vinyl alcohol) bond network, the tensile properties of the composite film were also improved by 30 %. Besides, the high specific surface area of biomass-derived porous biochar (2056 m²/g) can be obtained after carbonization of solid residues at 850 °C for 2 h, which was almost 8 times the specific surface area of the direct biomass carbonization due to the removal of lignin and hemicellulose. biomass-derived porous biochar can be used as an adsorbent, with a CO₂ capture capacity of 4.5 mmol g^-1 at normal temperature (25 °C, 1 bar). The filtrate after the reaction contained a large amount of hemicellulose oligomers, which can be reacted with dichloromethane at 170 °C for 1 h to obtain the furfural yield of 74 %. In summary, the proposed biorefinery scheme achieves a full-component upgrade of lignocellulose and can be further applied in various downstream fields.