Reduced-Toxicity and Highly Luminescent Germanium-Lead Perovskites Enabled by Strain Reduction for Light-Emitting
Yanjun Zhou1, Chen Zou2, Dingkun Peng3
1Institute of Advanced Magnetic Materials, College of Materials & Environmental Engineering, Hangzhou Dianzi University, Hangzhou 310018, China.
Abstract:
Germanium-lead (Ge-Pb) perovskites provide a promising solution for perovskite optoelectronic devices with reduced toxicity. However, Ge-Pb perovskite light-emitting diodes (PeLEDs) with >30 mol % Ge showed low emission efficiencies [Yang, D.; Zhang, G.; Lai, R.; Cheng, Y.; Lian, Y.; Rao, M.; Huo, D.; Lan, D.; Zhao, B.; Di, D. Germanium-Lead Perovskite Light-Emitting Diodes. Nat. Commun. 2021, 12 (1), 4295]. Here, we apply strain engineering to effectively improve the light emission efficiency and stability of Ge-Pb perovskite films and PeLEDs with 30 and 60 mol % Ge, through A-site modulation. The maximum external quantum efficiencies of the Ge-Pb PeLEDs with 30 and 60 mol % Ge are 8.5% and 3.0% at 3.32 mA cm-2 (∼922 cd m-2) and 0.53 mA cm-2 (∼60 cd m-2), respectively. Time-resolved transient absorption spectroscopy analysis of Ge-Pb perovskite films on different hole-transport layers shows that incorporating 30 mol % Ge into the perovskite with mixed A-site cations can effectively suppress trap-assisted recombination. Further analysis of their current density-voltage (J-V) curves reveals the efficiency loss mechanisms of Ge-Pb PeLEDs with high Ge fractions, indicating the possibility of further improvements.