Highly proton-conductive and low swelling polymeric membranes achieved by hydrophilic covalent cross-linking

Proton exchange membranes (PEMs) applied in fuel cell technology suffer from the trade-off between fast proton conduction and durable operation involving dimensional stability, mechanical strength, and oxidative resistance. To address this issue, a novel branched polybenzimidazole (brPBI) was synthesized, covalently cross-linked with (3-chloropropyl)triethoxysilane (CTS), and doped with a novel proton conductor FeATMP to prepare brPBI-CTS/FeATMP membranes. The branching degree of brPBI was optimized to achieve high molecular weight while the branching structure offered high free volume, abundant end-groups, and self-cross-linking moiety that enhanced proton conduction and dimensional/mechanical/oxidative stability. Covalent cross-linking with CTS enhanced the dimensional, mechanical, and oxidative stability while improving the water-assisted proton conduction owing to the hydrophilic nature of siloxane structure formed. At 180 ℃, the proton conductivity of the brPBI3-CTS/FeATMP composite membrane reached 0.136, 0.073, and 0.041 S cm^-1 at 100 % RH, 50 % RH, and 0 % RH, respectively, while its swelling ratio after immersion in water at 90 ℃ for 24 h was 4.69 %. The performance of the membranes demonstrated that construction of hydrophilic structure by covalent cross-linking was a successful strategy to break the trade-off effect for PEMs.