Developing Zn-2Cu-xLi (x < 0.1 wt %) alloys with suitable mechanical properties, degradation behaviors and...

Biodegradable Zn alloys show great potential for vascular stents due to their moderate degradation rates and acceptable biocompatibility. However, the poor mechanical properties limit their applications. In this study, low alloyed Zn-2Cu-xLi (x = 0.004, 0.01, 0.07 wt %) alloys with favorable mechanical properties were developed. The microstructure consists of fine equiaxed η-Zn grains, micron, submicron-sized and coherent nano ε-CuZn₄ phases. The introduced Li exists as a solute in the η-Zn matrix and ε-CuZn₄ phase, and results in the increase of ε-CuZn₄ volume fraction, the refinement of grains and more uniform distribution of grain sizes. As Li content increases, the strength of alloys is dramatically improved by grain boundary strengthening, precipitate strengthening of ε-CuZn₄ and solid solution strengthening of Li. Zn-2Cu-0.07Li alloy has the optimal mechanical properties with a tensile yield strength of 321.8 MPa, ultimate tensile strength of 362.3 MPa and fracture elongation of 28.0 %, exceeding the benchmark of stents. It also has favorable mechanical property stability, weak tension compression yield asymmetry and strain rate sensitivity. It exhibits uniform degradation and a little improved degradation rate of 89.5 μm∙year^-1, due to the improved electrochemical activity by increased ε-CuZn₄ volume fraction, and generates Li₂CO₃ and LiOH. It shows favorable cytocompatibility without adverse influence on endothelial cell viability by trace Li⁺. The fabricated microtubes show favorable mechanical properties, and stents exhibit an average radial strength of 118 kPa. The present study indicates that Zn-2Cu-0.07Li alloy is a potential and promising candidate for vascular stent applications. STATEMENT OF SIGNIFICANCE: Zn alloys are promising candidates for biodegradable vascular stents. However, improving their mechanical properties is challenging. Combining the advantages of Cu and trace Li, Zn-2Cu-xLi (x < 0.1 wt %) alloys were developed for stents. As Li increases, the strength of alloys is dramatically improved by refined grains, increased volume fraction of ε-CuZn₄ and solid solution of Li. Zn-2Cu-0.07Li alloy exhibits a TYS exceeding 320 MPa, UTS exceeding 360 MPa and fracture EL of nearly 30 %. It shows favorable mechanical stability, degradation behaviors and cytocompatibility. The alloy was fabricated into microtubes and stents for mechanical property tests to verify application feasibility for the first time. This indicates that Zn-2Cu-0.07Li alloy has great potential for vascular stent applications.