Design and optimization of a castability test for copper alloys applied to plaster moulds

Filip Radkovský1, František Zlámal1, Iveta Vasková2

  • 1Department of Metallurgical Technologies, VSB-Technical University of Ostrava, Faculty of Materials Science and Technology, 17. listopadu 2172/15, 708 00, Ostrava, Czech Republic.

Heliyon
|June 17, 2024
PubMed

Keywords:
CastabilityCooper alloyLost-wax castingPlaster mouldTechnological test

More Related Videos

Indirect Fabrication of Lattice Metals with Thin Sections Using Centrifugal Casting08:32

Indirect Fabrication of Lattice Metals with Thin Sections Using Centrifugal Casting

Published on: May 14, 2016

12.5K
Casting Protocols for the Production of Open Cell Aluminum Foams by the Replication Technique and the Effect on Porosity09:22

Casting Protocols for the Production of Open Cell Aluminum Foams by the Replication Technique and the Effect on Porosity

Published on: December 11, 2014

14.5K

Related Concept Videos

Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
131
Design Example: Managing Concrete Workability01:14

Design Example: Managing Concrete Workability

This example deals with managing the workability of concrete for a raft foundation project under hot weather conditions. Workability is crucial for ensuring the concrete is easy to place, compact, and finish. In this scenario, a slump test — a common method to measure the workability of fresh concrete — initially indicated low workability. This was attributed to the rapid water loss from the concrete mix, exacerbated by the high temperatures causing the course aggregates to heat up.
79
Slump Test01:20

Slump Test

The slump test is a widely used method to measure the workability of concrete. It employs a 12-inch high truncated cone mold that tapers from eight inches at the base to four inches at the top. Before testing, the mold is securely attached to a flat base and dampened.
Concrete is poured into the mold in three layers to conduct the test. Each layer is compacted 25 times with a steel tamping rod, which has a five-eighths-inch diameter and a rounded end, to ensure even distribution and eliminate...
200
Testing Water Quality01:14

Testing Water Quality

When the quality of water for concrete preparation is uncertain, its impact on the setting time of cement and compressive strength of mortar is assessed by comparison with de-ionized or distilled water benchmarks. American Society for Testing and Materials (ASTM) C1602 requires the setting times to be within 90 minutes of the control, British Standard (BS) 3146:1980 allows a 30-minute variance in the initial setting, while British Standards European Norm (BS EN) 1008 specifies initial setting...
105
Soundness of Cement01:17

Soundness of Cement

The soundness of cement refers to the ability of cement paste to retain its volume after setting. Unsound cement can lead to expansion and structural damage due to the presence of free lime, magnesia, and calcium sulfate. Free lime hydrates very slowly, expanding and causing unsoundness, which is difficult to detect because it intercrystallizes with other compounds. Magnesia also reacts with water, forming crystals that can disrupt the cement's structure. Calcium sulfate can create...
158