Ultrafast Microwave-Assisted Synthesis of Porous NiCo Layered Double Hydroxide Nanospheres for High-Performance...

Currently, new clean energy storage technology must be effective, affordable, and ecologically friendly so as to meet the diverse and sustainable needs of the energy supply. In this work, NiCo-LDH containing intercalated EG was successfully prepared within 210 s using an ultrafast microwave radiation technique. Subsequently, a series of characterization and systematic electrochemical tests were conducted to analyze the composition, structure, and energy storage mechanism of the NiCo-LDH material. The Ni:Co ratio of 5:5 results in the highest capacitance value of 2156 F/g at 1 A/g and an outstanding rate performance of 86.8% capacity retention rate at 10 A/g. The results demonstrated that the unique porous structure of NiCo-LDH and large layer spacing were conducive to more electrochemical reactions. Additionally, an electrochemical test was carried out on the NiCo-LDH as a hybrid supercapacitor electrode material, with NiCo-LDH-5:5 serving as the positive electrode and activated carbon as the negative electrode, the asymmetric supercapacitor can achieve a maximum energy density of 82.5 Wh kg^-1 and power density of 8000 W kg^-1. The NiCo-LDH-5:5//AC hybrid supercapacitors own 81.5% cycle stability and 100% coulombic efficiency after 6000 cycles at 10 A/g.