Preparation and Performance Evaluation of Self-Cementing Nanoscale Polymeric Microspheres with Salt and Temperature...

Polymer microspheres with temperature and salt resistance were synthesized using the anti-suspension polymerization method, incorporating the functional monomers AMPS, AM, and AA. To enhance their self-gelling properties, the microspheres were designed with a core-shell structure. The shell is composed of a polymeric surfactant, fatty alcohol polyoxyethylene ether methacrylate (AEOMA), which serves as a thermosensitive crosslinking agent, enabling self-crosslinking upon shell decomposition, addressing compatibility with reservoir pore throat dimensions. Comprehensive characterizations including infrared spectroscopy, scanning electron microscopy, optical microscopy, and laser particle size analysis were conducted. The microspheres exhibited successful synthesis, a nanoscale size, and regular spherical morphology. They demonstrated excellent temperature and salt resistance, making them suitable for high-temperature, high-salinity reservoir profile control. With a stable three-dimensional network structure, the microspheres displayed good expansion behavior due to hydrophilic groups along the polymer chains, resulting in favorable water affinity. Even after aging, the microspheres maintained their gelling state with a distinct and stable microscopic network skeleton. They exhibited superior plugging performance in low-permeability reservoirs, while effectively improving water absorption profiles in reservoirs with permeability contrasts of 10 to 80, thereby enhancing oil recovery.