Fabrication of Ceramic Microchannels with Periodic Corrugated Microstructures as Catalyst Support for Hydrogen
Xinying Li1, Chao Gao1, Ding Yuan1
1Pen-Tung Sah Institute of Micro-Nano Science and Technology, Xiamen University, Xiamen 361005, China.
Abstract:
Hydrogen energy is the clean energy with the most potential in the 21st century. The microchannel reactor for methanol steam reforming (MSR) is one of the effective ways to obtain hydrogen. Ceramic materials have the advantages of high temperature resistance, corrosion resistance, and high mechanical strength, and are ideal materials for preparing the catalyst support in microchannel reactors. However, the structure of ceramic materials is hard and brittle, and the feature size of microchannel is generally not more than 1 mm, which is difficult to process using traditional processing methods. Diamond wire saw processing technology is mainly used in the slicing of hard and brittle materials such as sapphire and silicon. In this paper, a microchannel with a periodic corrugated microstructure was fabricated on a ceramic plate using diamond wire sawing, and then as a catalyst support when used in a microreactor for MSR hydrogen production. The effects of wire speed and feed speed on the amplitude and period size of the periodic corrugated microstructure were studied using a single-factor experiment. The microchannel surface morphology was observed via SEM and a 3D confocal laser microscope under different processing parameters. The microchannel samples obtained under different processing parameters were supported by a multiple impregnation method. The loading strength of the catalyst was tested via a strong wind purge experiment. The experimental results show that the periodic corrugated microstructure can significantly enhance the load strength of the catalyst. The microchannel catalyst support with the periodic corrugated microstructure was put into the microreactor for a hydrogen production experiment, and a good hydrogen production effect was obtained. The experimental results have a positive guiding effect on promoting ceramic materials as the microchannel catalyst support for the development of hydrogen energy.