Experimental Research on Gradation Range and Performance of SMAC13

Stone matrix asphalt and asphalt concrete mixture with 13.2 mm nominal maximum aggregate size (named SMA13 and AC13, respectively) are widely used in the surface course of asphalt pavement in China. Generally, the pavement performance of SMA13 is superior to that of AC13, while the cost of the former is significantly higher than that of the latter. The objective of this paper was to develop a new hot mix asphalt (named SMAC13) whose performance and cost are between SMA13 and AC13. A boundary sieve size (BSS) of 2.36 mm was selected between fine and coarse aggregates. Based on the union set of aggregate gradation ranges of SMA13 and AC13, the family of gradation curves in the forms of S shapes were designed in terms of the BSS passing rate. According to the evaluation of the skeleton interlock of coarse aggregate of the gradation curve family, the aggregate gradation range of SMAC13 was determined. Also, the performance of three kinds of asphalt mixtures were compared through laboratory tests. The results indicated that SMA13 shows the best rutting resistance, followed by SMAC13 then AC13, while in terms of low-temperature performance in resistance to cracking, the sequence is SMAC13, AC13, and SMA13. The sequence of water stability is AC13, SMAC13, and SMA13. Furthermore, the cost of SMAC13 is 25% less than that of SMA13. Therefore, SMAC13 can be used as an alternative for the surface course of asphalt pavement in terms of performance and cost.