Minimization of Energy Level Mismatch of PCBM and Surface Passivation for Highly Stable Sn-Based Perovskite Solar...

Developing high-performance and stable Sn-based perovskite solar cells (PSCs) is difficult due to the inherent tendency of Sn²⁺ oxidation and, the huge energy mismatch between perovskite and Phenyl-C61-butyric acid methyl ester (PCBM), a frequently employed electron transport layer (ETL). This study demonstrates that perovskite surface defects can be passivated and PCBM's electrical properties improved by doping n-type polymer N2200 into PCBM. The doping of PCBM with N2200 results in enhanced band alignment and improved electrical properties of PCBM. The presence of electron-donating atoms such as S, and O in N2200, effectively coordinates with free Sn²⁺ to prevent further oxidation. The doping of PCBM with N2200 offers a reduced conduction band offset (from 0.38 to 0.21 eV) at the interface between the ETL and perovskite. As a result, the N2200 doped PCBM-based PSCs show an enhanced open circuit voltage of 0.79 V with impressive power conversion efficiency (PCE) of 12.98% (certified PCE 11.95%). Significantly, the N2200 doped PCBM-based PSCs exhibited exceptional stability and retained above 90% of their initial PCE when subjected to continuous illumination at maximum power point tracking for 1000 h under one sun.