Evaluation of artifacts produced by conventional dental materials in standard and high-resolution CBCT imaging

The aim of this study was to identify and quantify artifacts produced by commonly used dental restorative materials in both standard and high-resolution cone beam computed tomographic imaging. In this in vitro study, 25 different dental materials were placed in holes (3 mm in diameter × 2 mm thick) prepared in the center of 10 × 10-mm polymethyl methacrylate plates. The specimens, along with a control plate prepared with an unfilled hole, were scanned at standard and high resolutions. The gray values (GVs) of the specimens were measured at 1-, 2-, 4-, and 8-mm distances from the material surfaces, and in 8 different directions, resulting in 32 measurements per specimen. The absolute value of the difference (ΔGV) between the GV of each measurement point on the specimen disc and the GV of the corresponding point on the control disc was considered to be the number of artifacts at that point. The median ΔGV of each material was calculated, and the materials were then ranked in terms of artifact formation using the Kruskal-Wallis test. At standard resolution, the greatest numbers of artifacts were caused by AH 26 root canal sealer and Heraenium S nickel-chromium alloy, and the fewest were caused by Whitepost DC #3 glass fiber post and ChemFil Superior glass ionomer cement. At high resolution, the greatest numbers of artifacts were found in amalgam (admix; SDI) and Heraenium S, and the fewest in Whitepost DC and GC Initial enamel porcelain. The median ΔGV values at standard and high resolutions were 46.0 and 57.0, respectively. High and standard resolutions were significantly different in terms of artifact formation (P = 0.001; Wilcoxon test). AH 26 sealer was the only material that demonstrated a statistically significant reduction in artifact formation at high resolution compared with standard resolution (P = 0.05; Wilcoxon test). The number of artifacts produced by dental materials at both resolutions decreased with an increasing distance from the surface of the material.