Fatigue Test Method to Evaluate the 50 Year Durability of Venous Stents

Iliofemoral venous obstructive disease can result in significant, potentially debilitating symptoms that can negatively affect quality of life. Unlike arterial disease, patients with deep venous disease have a significantly lower median age, therefore the need for long term stent patency becomes a matter of decades rather than years. Furthermore, iliofemoral lesions frequently require stent placement across the inguinal ligament. Such stents are subject to dynamic stress from leg movement and associated concerns for device fatigue, resulting in stent fracture. The aim of this study was to describe an in vitro 50 year stent fatigue test method designed to assess durability against dynamic stress induced device fracture.

Through literature review, cadaver studies, and computer modelling, the most challenging loading was confirmed to be hip flexion across the inguinal ligament. This occurs when the patient adjusts between a seated and standing position. Sit to stand hip flexion at the inguinal ligament was effectively simulated on the bench in this in vitro experimental study.

When tested under challenge parameters, hip flexion was reliably found to cause fractures in non-venous nitinol stents. However, a dedicated self expanding nitinol venous stent, engineered for improved durability, underwent up to 50 years of simulated loading on the bench with 15% (3/20) of stents experiencing fractures at 50 years, compared with fractures in 35% (14/40) of non-venous stents tested to 1.4 years; no statistical testing was performed as durations do not match and the objective was to demonstrate the test method.

The presented fatigue test method is a suitable approach for evaluating the durability of stents intended for venous use. Venous stents demonstrated superior fatigue resistance compared with non-venous stents via in vitro hip flexion testing.