Enhancing mechanical and water barrier properties of starch film using chia mucilage

Biodegradable packaging materials are increasingly being investigated due to rising concerns about food safety and environmental conservation. This study examines the incorporation of chia mucilage (CM) into starch-based films using the casting method, aiming to understand its effects on the structure and functionality of the films. CM, an anionic heteropolysaccharide, is hypothesized to enhance the mechanical and barrier properties of the films through polymer interactions and hydrogen bonding. Our findings confirm that CM incorporation results in films with uniformly smooth surfaces, indicating high compatibility and homogeneity within the starch matrix. Notably, CM improves film transparency and crystallinity. Mechanical assessments show a remarkable elevation in tensile strength, soaring from 5.21 MPa to 12.38 MPa, while elongation at break decreases from 61.73 % to 31.42 %, indicating a trade-off between strength and flexibility. Additionally, water solubility decreases from 57.97 % to 41.40 %, and water vapor permeability is reduced by 30 % with CM loading. These results highlight the role of CM in facilitating the formation of a dense, interconnected polymeric network within the starch matrix. Given the soluble dietary fiber nature of CM, the CS/CM (corn starch/chia mucilage) blended films are expected to be safe for food packaging and applicable as edible films with health benefits.