Enhancing oxygen reduction activity of dinuclear copper complexes loaded on an N-doped carbon support via a...

Bioinspired by the active sites of multicopper oxidases (MCOs), bi/multinuclear copper complexes have attracted great attention in promoting catalytic activity for the oxygen reduction reaction (ORR). Herein, we report the preparation of a Cu-N-C electrocatalyst Cu-BPOZ@CNB-400 for efficient ORR, which was obtained by low temperature pyrolysis of a dinuclear 2,5-bis(2-pyridyl)-1,3,4-oxadiazole (BPOZ) copper complex loaded on a N-doped carbon support at 400 °C. Cu-BPOZ@CNB-400 exhibited a half-wave potential (E_1/2) of 0.86 V vs. RHE for the ORR in 0.1 M KOH solution, which was significantly higher than that of the Cu-BPOZ@CNB-800 (E_1/2 = 0.83 V) catalyst treated under high temperature (at 800 °C) and the control catalyst Cu-Phen@CNB-400 (E_1/2 = 0.82 V) derived from low-temperature-treatment (at 400 °C) of a mononuclear phenanthroline-coordinated-Cu complex loaded on a N-doped carbon support. When Cu-BPOZ@CNB-400 was applied as the cathode catalyst in zinc-air batteries a maximum power density (P_max) of 127 mW cm^-2 could be achieved, demonstrating comparable catalyst performance to the commercial 20 wt% Pt/C (P_max = 122 mW cm^-2) and the control Cu-Phen@CNB-400 catalyst (P_max = 105 mW cm^-2) under similar experimental conditions. Low-temperature pyrolysis of dinuclear copper complexes on a carbon support improved the charge transfer efficiency, inhibited metal aggregation, and could produce highly dispersed Cu-N-C catalysts with dinuclear copper sites for promoting the 4e^--reduction selectivity of the ORR. It thus provides a cost-effective approach for the controllable fabrication of efficient ORR catalysts to be applied for energy conversion devices.