PVA Hydrogels Supplemented with PLA Mesh for Tissue Regeneration Scaffold

This study examined the tensile strength and biocompatibility properties of polyvinyl alcohol (PVA) hydrogel tissue regeneration scaffolds with polylactic acid (PLA) mesh fabric added as reinforcement, with a focus on the impact of heat treatment temperature and the number of layers of the PLA mesh fabric. The hydrogel scaffolds were prepared using a freeze-thaw method to create PVA hydrogel, with the PLA mesh fabric placed inside the hydrogel. The swelling ratio of the PVA/PLA hydrogel scaffolds decreased with increasing layer number and heat treatment temperature of the PLA mesh. The gel strength was highest when five layers of PLA mesh fabric were added, heat-treated at 120 °C, and confirmed to be properly placed inside the hydrogel by SEM images. The MTT assay and DAPI staining using HaCaT cells demonstrated that the cell proliferation was uninterrupted throughout the experimental period, confirming the biocompatibility of the scaffold. Therefore, we confirmed the possibility of using PLA mesh fabric as a reinforcement for PVA hydrogel to improve the strength of scaffolds for tissue regeneration, and we confirmed the potential of PLA mesh fabric as a reinforcement for various biomaterials.