A Novel Fracturing Fluid Based on Functionally Modified Nano-Silica-Enhanced Hydroxypropyl Guar Gel

Considering the damage caused by conventional fracturing fluid in low-permeability reservoirs, a novel fracturing fluid (FNG) combining hydroxypropyl guar (HPG) and functionally modified nano-silica (FMNS) was prepared. The properties of heat/shear resistance, rheological property, proppant transportation, and formation damage were evaluated with systematic experiments. The results showed that the viscosities of FNG before and after the heat/resistance were 1323 mPa·s and 463 mPa·s, respectively, while that of conventional HPG gel was 350 mPa·s. FNG is a pseudoplastic strong gel with a yield stress of 12.9 Pa, a flow behavior index of 0.54, an elastic modulus of 16.2 Pa, and a viscous modulus of 6.2 Pa. As the proportions of proppant mass in further sections transported with FNG were higher than those transported with HPG gel, FNG could transport the proppant better than HPG gel at high temperatures. Because of the amphiphilic characteristics of FMNS, the surface/interface properties were improved by the FNG filtrate, resulting in a lower oil permeability loss rate of 10 percentage points in the matrix than with the filtrated HPG gel. Due to the considerable residual gel in broken HPG gel, the retained conductivity damaged with broken FNG was 9.5 percentage points higher than that damaged with broken HPG gel. FNG shows good potential for reducing formation damage during fracturing in low-permeability reservoirs in China.