Specific Condis Crystal-like Mesophase of Poly(butylene succinate-co-butylene adipate)

Understanding the properties of polymers, such as their crystallinity, is crucial for their material performance and predicting their behavior during and after use, especially in the case of environmentally friendly (bio)degradable polymers, enabling optimized design. In this work, for the first time, a pressure-induced condis crystal-like mesophase of poly(butylene succinate-co-butylene adipate) (PBSA) is presented. The phase behavior of pressed films obtained from commercial PBSA with 25% butylene adipate units is investigated at various processing temperatures from room temperature to 100 °C, pressed at a pressure of the press jaws and at 2-5 t for 1-5 min. The characterization and quantification evaluation of the condis crystal-like mesophase of pressed PBSA formed at temperatures above the glass transition is investigated by X-ray diffraction, polarized optical microscopy (POM), and differential scanning calorimetry (DSC) methods. Our results demonstrate that pressed PBSA films at 60 °C show a condis crystal-like mesophase, characterized by the presence of reflections at wide angles, birefringence by POM, as well as a higher melting point (endotherm) by DSC. The resulting oriented mesomorphic green polymer can, in a sustainable manner, expand further technological applications of (bio)degradable polymers, especially in the medical field, and open up opportunities for further research that could provide such polymers with tailored persistence and degradation, thus changing the shelf life.