Effect of Mixed Morphology (Simple Cubic, Face-Centered Cubic, and Body-Centered Cubic)-Based Electrodes on the...

Supercapacitors store energy due to the formation of an electric double layer (EDL) at the interface of the electrodes and electrolyte. The present article deals with the finite element study of equilibrium electric double layer capacitance (EDLC) in the mixed morphology electrodes comprising all three fundamental crystal structures, simple cubic (SC), body-centered cubic (BCC), and face-centered cubic morphologies (FCC). Mesoporous-activated carbon forms the electrode in the supercapacitor with (C₂H₅)₄NBF₄/propylene carbonate organic electrolyte. Electrochemical interference is clearly demonstrated in the supercapacitors with the formation of the potential bands, as in the case of interference theory due to the increasing packing factor. The effects of electrode thickness varying from a wide range of 50 nm to 0.04 mm on specific EDLC have been discussed in detail. The interfacial geometry of the unit cell in contact with the electrolyte is the most important parameter determining the properties of the EDL. The critical thickness of the electrodes is 1.71 μm in all the morphologies. Polarization increases the interfacial potential and leads to EDL formation. The Stern layer specific capacitance is 167.6 μF cm^-2 in all the morphologies. The maximum capacitance is in the decreasing order of interfacial geometry, as FCC > BCC > SC, dependent on the packing factor. The minimum transmittance in all the morphologies is 98.35%, with the constant figure of merit at higher electrode thickness having applications in the chip interconnects. The transient analysis shows that the interfacial current decreases with increasing polarization in the EDL. The capacitance also decreases with the increase of the scan rate.