A self-healing thermogelling polymer with tunable transparency based on biomolecule alginate grafting phenylboronic
Hongdong Wang1, Qi Wang2, Kunpeng Wang3
1School of Mechatronic Engineering and Automation, Shanghai University, Shanghai 200444, China; Key Laboratory of Advanced Display and System Application, Ministry of Education, Shanghai 200444, China; State Key Laboratory of Tribology in Advanced Equipment, Tsinghua University, Beijing 100084, China.
Abstract:
Thermogelling polymers with transparency, structure stability and biocompatibility are promising for biomedicine application. In this study, a thermogelling polymer P-C5PEG with tunable transparency was developed by the reaction between alternating copolymer C5PEG and chemically modified biomolecule Alg-PBA via boronic ester bonds. The sol-to-gel transition of P-C5PEG aqueous solution sensitively responded to changes in temperature, and the critical value could be adjusted between 15 and 40 °C by varying the content of C5PEG and Alg-PBA. As the weight ratio of Alg-PBA to C5PEG was over 0.3, the transparency of as-synthesized hydrogel kept above 75 % at 37 °C. Meanwhile, immersion P-C5PEG hydrogel in CaCl2 solution significantly increased its mechanical strength by 3 times due to chelation effect. The shear-resistance and self-healing properties were ensured by dynamic boronic ester bonds due to the protective effect of hydrophobic gel network. As a drug delivery, P-C5PEG hydrogel had a swelling rate of 3748.7 ± 103 % in PBS and could continuously release fluorescein sodium within 24 h. Moreover, the in vitro degradability and cytotoxicity of P-C5PEG was confirmed. Finally, the mechanisms behind the thermogelling property and tunable transparency were revealed. Overall, this thermogelling P-C5PEG polymer, with tunable transparency and thermo-responsiveness, exhibits great potential for biomedicine application.