Discarded enoki mushroom root-derived multifunctional chrome-free chitosan-based tanning agent for eco-leathers...

The aim of this study was to develop new discarded enoki mushroom root-derived multifunctional chrome-free chitosan-based tanning agents that can be used for eco-leather manufacturing. In this study, oligochitosan (OCS) was prepared from chitosan extracted from the enoki mushrooms and chemically modified using reactive dye R19 and epichlorohydrin (ECH) to prepare chromium-free tanning agent (OCS-R19-ECH) with both tanning and dyeing functions. FT-IR, XRD, and NMR (¹H) confirmed the successful synthesis of the product. The molecular weight of OCS-R19-ECH is 6355 g/mol, with an average particle size of 1249.37 nm and an epoxy value of 0.276 mol/100 g. OCS-R19-ECH was used for tanning experiments on bated sheepskin, and the results showed that the leather tanned with OCS-R19-ECH not only exhibited excellent wet-heat stability (shrinkage temperature = 81 °C), but also superior dyeing uniformity, resistance to dry and wet abrasion, mechanical strength (tensile strength = 12.4 MPa, tear strength = 57.3 N/mm), and outstanding antimicrobial properties. Most importantly, compared with traditional tanning agents, OCS-R19-ECH has a higher pH (9.0), tanning-dyeing integration, non-acid soaking, and non-basifying can be achieved in leather making, which can greatly simplify the tanning processes. This new multifunctional chrome-free chitosan-based tanning agent facilitates high-value utilization of waste resources.