Compressive Properties of Basalt Fibers and Polypropylene Fiber-Reinforced Lightweight Concrete

With the development of high-rise and large-scale modern structures, traditional concrete has become a design limitation due to its excessive dead weight. High-strength lightweight concrete is being emphasized. Lightweight concrete has low density and the characteristics of a brittle material. This is an important factor affecting the strength and ductility of the lightweight concrete. To improve these shortcomings and proffer solutions, a three-phase composite lightweight concrete was prepared using a combination of tumbling and molding methods. This paper investigates the various influencing factors such as the stacking volume fraction of GFR-EMS, the type of fiber, and the content and length of fiber in the matrix. Studies have shown that the addition of fibers significantly increases the compressive strength of the concrete. The compressive strength of concrete with a 12 mm basalt fiber (BF) (1.5%) admixture is 9.08 MPa, which is 62.43% higher than that of concrete without the fiber admixture. The compressive strength was increased by 27.53 and 21.88% compared to concrete containing 3 mm BF (1.5%) and 0.5% BF (12 mm), respectively. Fibers can fill the pore defects within the matrix. Mutually overlapping fibers easily form a network structure to improve the bond between the cement matrix and the aggregate particles. The compressive strength of lightweight concrete with the addition of BF was 16.71% higher than that with the addition of polypropylene fiber (PPF) with the same length and content of fibers. BF has been shown to be more effective in improving the mechanical properties of concrete. In this work, the compressive mechanism and optimum preparation parameters of a three-phase composite lightweight concrete were analyzed through compression tests. This provides some insights into the development of lightweight concrete.