Improving the Oxygen Evolution Reaction Kinetics in Zn-Air Battery by Iodide Oxidation Reaction

Zinc-air batteries (ZABs) have garnered considerable attention as a highly promising contender in the field of energy storage and conversion. Nevertheless, their performance is considerably impeded by the proliferation of dendrites on the Zinc anode and the slow kinetics of the redox reaction on the air cathode. Herein, taking Ag_30%@LaCoO₃ (Ag_30%@LCO) heterojunction catalyst as the cathode, it is demonstrated that adding KI additives to the alkaline electrolyte can not only enhance the oxygen electrocatalytic reaction but also inhibit the formation of zinc anode dendrites, thereby achieving a comprehensive improvement in the performance of ZABs. Under the action of the KI additive, the optimized Ag_30%@LCO catalyst shows a decreased overpotential from 460 to 220 mV at j = 10 mA cm^-2, while the assembled ZAB shows reduced charging potential (1.8 V), and long cycle stability (180 h). Furthermore, the morphology characterization results indicate a reduction in dendrites on the Zn anode. Both experimental and calculated results indicate that the presence of I^- as a reaction modifier alters the trajectory of the conventional oxygen evolution reaction, resulting in a more thermodynamically favorable pathway. The introduction of KI additives as electrolytes provides a straightforward approach to developing comprehensively improved ZABs.