The Synthesis and Characterization of Selenium-Doped Bioglass

Background Bioactive glass, which can form strong bonds with tissues, particularly bones, has become pivotal in tissue engineering. Incorporating biologically active ions like selenium enhances its properties for various biomedical applications, including bone repair and cancer treatment. Selenium's antioxidative properties and role in bone health make it a promising addition to biomaterial. Aim The present study was aimed at the preparation and characterization of selenium-doped bioglass. Materials and methods Tetraethyl orthosilicate (TEOS) was mixed with ethanol, water, and nitric acid to form a silica network and then supplemented with calcium nitrate, selenium acid sodium nitrate, and orthophosphoric acid. Sequential addition ensured specific functionalities. After sintering at 300 °C for three hours, the viscous solution transformed into powdered selenium-doped bioglass. Characterization involved scanning electron microscope (SEM) for microstructure analysis, attenuated total reflection infrared spectroscopy (ATR-IR) for molecular structure, and X-ray diffraction (XRD) for crystal structure analysis. Results SEM analysis of selenium-doped bioglass reveals a uniform distribution of selenium dopants in an amorphous structure, enhancing bioactivity through spherical particles with consistent size, micro-porosity, and roughness, facilitating interactions with biological fluids and tissues. ATR-IR analysis shows peaks corresponding to Si-O-Si and P-O bonds, indicating the presence of phosphate groups essential for biomedical applications within the bioglass network. XRD analysis confirms the amorphous nature of selenium-doped bioglass, with shifts in diffraction peaks confirming selenium incorporation without significant crystallization induction. Conclusion The selenium-infused bioglass displays promising versatility due to its amorphous structure, potentially enhancing interactions with biological fluids and tissues. Further research is needed to assess its impact on bone regeneration activity.