Experimental, theoretical and numerical simulation-based investigations on the fabricated Cu₂ZnSn thin-film-based...

Copper-zinc-tin Cu₂ZnSn (CZT) thin films are promising materials for solar cell applications. This thin film was deposited on a fluorine-doped tin oxide (FTO) using an electrochemical deposition hierarchy. X-ray diffraction of thin-film studies confirms the variation in the structural orientation of CZT on the FTO surface. As the pH of the solution is increased, the nature of the CZT thin-film aggregate changes from a fern-like leaf CZT dendrite crystal to a disk pattern. The FE-SEM surface micrograph shows the dendrite fern leaf and sharp edge disks. The 2-D diffusion limitation aggregation under slippery conditions for ternary thin films was performed for the first time. The simulation showed that by changing the diffusing species, the sticking probability was responsible for the pH-dependent morphological change. Convincingly, diffusion-limited aggregation (DLA) simulations confirm that the initial structure of copper is responsible for the final structure of the CZT thin films. An experimental simulation with pH as a controlled parameter revealed phase transition in CZT thin films. The top and back contact of Ag-CZT thin films based on Schottky behavior give a better electronic mechanism in superstrate and substrate solar cells.