Introduction of polymeric ionic liquids containing quaternary ammonium groups to construct high-temperature proton...

A series of membrane materials suitable for high-temperature proton exchange membranes (HT-PEM) were successfully prepared by introducing polymeric ionic liquids (PILs) containing quaternary ammonium groups into ether-bonded polybenzimidazole (OPBI). The structure of the cross-linked membrane has a strong interaction with phosphoric acid (PA), which enhances proton transport and PA retention. To ensure better overall performance of the cross-linked membrane, the optimal PIL content is 30 wt% (OPBI-PIL-30 %). The PA uptake of OPBI-PIL-30 % membrane was 323.24 %, and the proton conductivity at 180 ℃ was 113.94 mS cm^-1, which was much higher than that of OPBI membrane. It is noteworthy that the PA retention of OPBI-PIL-30 % membrane could reach 71.38 % after 240 h of testing under the harsh environment of 80 ℃/40 % RH. The membrane showed better acid retention capacity of 86.89 % at 160 ℃ under anhydrous environment. The OPBI-PIL-20 % membrane achieved the maximum power density of 436.19 mW cm^-2, attributed to its favorable mechanical characteristics and proton conductivity. By these excellent properties, it is shown that OPBI-PIL-X membranes containing quaternary ammonium groups have the potential to be applied in high temperature proton exchange membrane fuel cells (HT-PEMFCs).