Modification of polyvinylidene fluoride membrane with ciprofloxacin to improve the bacteriostatic performance

The common polyvinylidene fluoride (PVDF) membrane itself is susceptible to membrane fouling, especially biofouling, which is a serious threat. In this study, PVDF membrane was modified with ciprofloxacin (CIP) through co-blending to investigate the filtration properties, bacterial inhibition and fouling resistance. Modified membranes were prepared by adding 0.3 g (M_C0.3), 0.6 g (M_C0.6), 0.9 g (M_C0.9) and 1.2 g (M_C1.2) CIP per 100 g casting solution. Among these modified membranes, M_C0.6 showed the best filtration performances, with the pure water flux stabilized at about 416.67 L/(m²·h) and bovine serum albumin (BSA) rejection of 92.0% at a trans-membrane pressure of 0.1 MPa. The pore size was reduced, the average roughness was reduced to 29.4 nm, the contact angle was lowered to 68.9°, and the hydrophilicity was greatly improved. The width of the inhibition circle produced by M_C0.6 was 0.35-0.45 mm, and the modified membrane showed good inhibition of non-specific bacteria and algal removal during urban river water filtration. The rejection of BSA was increased by 16.32% compared to the base membrane and the adsorption rate for BSA was reduced by 68.45%. In addition, the removal of conventional pollutants in urban river water by the modified membranes for was also improved. Compared with that of the base membrane, the removal of TN, NH₃-N, TP and COD by M_C0.6 was increased by 10.58%, 12.45%, 15.44% and 13.53%. The results showed that CIP co-blending modified PVDF membrane could effectively improve membrane performances and has good value for water treatment.