3-Pentadecylphenol (PDP) as a Novel Compatibilizer for Simultaneous Toughened and Reinforced PA10,12 Composites

The utilization of polyamide 10,12 (PA10,12) composites in various industries has been limited constrained by their inherent low toughness, making it a challenge to achieve a balance between toughness and structural integrity through conventional elastomer addition strategies. Herein, we introduce a straightforward method for the concurrent toughening and reinforcement of PA10,12 composites. This is accomplished by blending polyolefin elastomer (POE) and 3-pentadecylphenol (PDP) with the PA10,12 matrix. The incorporation of 5 wt% PDP effectively blurred the PA10,12/POE interface due to PDP's role as a compatibilizer. This phenomenon is attributed to the formation of intermolecular hydrogen bonds, as evidenced by Fourier Transform Infrared Spectroscopy (FTIR) analysis. Further investigation, using differential scanning calorimetry (DSC), elucidated the crystallization thermodynamics and kinetics of the resulting binary PA10,12/POE and ternary PA10,12/POE/PDP composites. Notably, the crystallization temperature (T) was observed to decrease from 163.1 °C in the binary composite to 161.5 °C upon the addition of PDP. Increasing the PDP content to 10% led to a further reduction in T to 159.5 °C due to PDP's capacity to slow down crystallization. Consequently, the ternary composite of PA10,12/POE/PDP (92/3/5 wt%) demonstrated a synergistic improvement in mechanical properties, with an elongation at break of 579% and a notch impact strength of 61.54 kJ/m². This represents an approximately eightfold increase over the impact strength of unmodified PA10,12. Therefore, our work provides the potential of PDP as a compatibilizer to develop nylon composites with enhanced stiffness and toughness.