Evaluating the osteogenic properties of polyhydroxybutyrate-zein/multiwalled carbon nanotubes (MWCNTs) electrospun...

In this investigation, the electrospun nanocomposite scaffolds were developed utilizing poly-3-hydroxybutyrate (PHB), zein, and multiwalled carbon nanotubes (MWCNTs) at varying concentrations of MWCNTs including 0.5 and 1 wt%. Based on the SEM evaluations, the scaffold containing 1 wt% MWCNTs (PZ-1C) exhibited the lowest fiber diameter (384 ± 99 nm) alongside a suitable porosity percentage. The presence of zein and MWCNT in the chemical structure of the scaffold was evaluated by FTIR. Furthermore, TEM images revealed the alignment of MWCNTs with the fibers. Adding 1 % MWCNTs to the PHB-zein scaffold significantly enhanced tensile strength by about 69 % and reduced elongation by about 31 %. Hydrophilicity, surface roughness, crystallinity, and biomineralization were increased by incorporating 1 wt% MWCNTs, while weight loss after in vitro degradation was decreased. The MG-63 cells exhibited enhanced attachment, viability, ALP secretion, calcium deposition, and gene expression (COLI, RUNX2, and OCN) when cultivated on the scaffold containing MWCNTs compared to the scaffolds lacking MWCNTs. Moreover, the study found that MWCNTs significantly reduced platelet adhesion and hemolysis rates below 4 %, indicating their favorable anti-hemolysis properties. Regarding the aforementioned results, the PZ-1C electrospun composite scaffold is a promising scaffold with osteogenic properties for bone tissue engineering applications.