Weak static magnetic fields facilitated highly efficient 2,4,6-trichlorophenol removal by sulfurized nanoscale...

Sulfurized nanoscale zero-valent iron supported on biochar (BC-SNZVI) has been successfully synthesized for 2,4,6-trichlorophenol (2,4,6-TCP) removal, while was only effectively under acidic conditions. To obtain highly efficient removal of 2,4,6-TCP within a broader pH range, weak static magnetic fields (WMF) was applied in BC-SNZVI/2,4,6-TCP aqueous systems. Results showed 30 mT WMF supported the most extensive 2,4,6-TCP removal, and 87.4% of 2,4,6-TCP (initial concentration of 30 mg/L) was removed by 0.5 g/L BC-SNZVI at neutral pH (pH = 6.8) within 180 min, which was increased by 54.4% compared to that without WMF. The observed rate constant (K_obs) under 30 mT WMF was 2.1-fold greater than that without WMF. Although three typical anions (NO₃^- (0.5-10.0 mM), H₂PO₄^- (0.05-0.5 mM), and HCO₃^- (0.5-5.0 mM)) still inhibited 2,4,6-TCP removal, WMF could efficiently alleviate the inhibitory effects. Moreover, 73.1% of 2,4,6-TCP was successfully removed by BC-SNZVI under WMF in natural water. WMF remarkably boosted the dechlorination of 2,4,6-TCP, increasing the 2,4,6-TCP dechlorination efficiency from 45.2% (in the absence of WMF) to 83.8% (in the presence of WMF) by the end of 300 min. And the complete dechlorination product phenol appeared within 10 min. Force analysis confirmed the magnetic field gradient force (F_B) moved paramagnetic Fe²⁺ at the SNZVI surface along the direction perpendicular to the external applied field, promoting the mass-transfer controlled SNZVI corrosion. Corrosion resistance analysis revealed WMF promoted the electron-transfer controlled SNZVI corrosion by decreasing its self-corrosion potential (E_corr). With the introduction of sulfur, the magnitude of F_B doubled and the E_corr decreased comparing with NZVI. Our findings provide a facile and viable strategy for treating chlorinated phenols at neutral pH.