Adsorption performance and mechanism of a starch-stabilized ferromanganese binary oxide for the removal of phosphate

Effective removal of phosphate from water is essential for preventing the eutrophication and worsening of water quality. This study aims to enhance phosphate removal by synthesizing starch-stabilized ferromanganese binary oxide (FMBO-S), discover the factors, and investigate adsorption mechanisms. FMBO and FMBO-S properties were studied using Scanning Electron Microscopy, BET analysis, Polydispersity Index (PDI), Fourier Transform Infrared Spectroscopy, and X-ray Photoelectron Spectroscopy (XPS). After starch loading, the average pore diameter increased from 14.89 Å to 25.16 Å, and significantly increased the pore volume in the mesopore region. FMBO-S showed a PDI value below 0.5 indicating homogeneous size dispersity and demonstrated faster and higher adsorption capacity: 61.24 mg g^-1 > 28.57 mg g^-1. Both FMBO and FMBO-S adsorption data fit well with the pseudo-second-order and Freundlich models, indicating a chemisorption and multilayered adsorption process. The phosphate adsorption by FMBO was pH-dependent, suggesting electrostatic attraction as the dominant mechanism. For the FMBO-S, phosphate adsorption was favored in a wide pH range, despite the weaker electrostatic attraction as evident from the point of zero charge and zeta potential values, indicating ligand exchange as a main mechanism. Moreover, the XPS analysis shows a significant change in the proportion of Fe species for FMBO-S than FMBO after phosphate adsorption, indicating significant involvement of Fe. Meanwhile, phosphate adsorption was almost unaffected by the presence of Cl^-, NO₃^-, and SO₄^2- anions, whereas CO₃^2- significantly reduced the adsorption capacity. This study revealed that FMBO-S could be a promising, low-cost adsorbent for phosphate removal and recovery from water.