Anisotropic Chitosan-nanocellulose/Zeolite imidazolate frameworks-8 aerogel for sustainable dye removal

Assembling microscopic metal-organic frameworks into macroscopic polymeric scaffolds to develop highly renewable materials has been a promising yet challenging area of research. Herein, chitosan (CS) blended with nano-cellulose (NC) was unidirectionally transformed into an aerogel with oriented macropores and then biomineralized with zeolite imidazolate frameworks-8 (ZIF-8) to form a hierarchical structured chitosan-nanocellulose/zeolite imidazolate frameworks-8 (CS-NC-ZIF-8) hybrid aerogel. Incorporating ZIF-8 significantly increases the versatility and mechanical strength with a Young's modulus of 14.18 MPa of the CS-NC aerogel. The incorporation of ZIF-8 into the aerogel not only enhances its adsorption capacity for methylene blue, rhodamine B, acid fuchsin, and methyl orange, but also facilitates the generation of electrons from water that can be transferred to degrade > 90 % of malachite green within 90 min in each catalytic cycle, and this capability was maintained for at least 10 consecutive cycles. Remarkably, the hybrid aerogel was highly renewable after the adsorption of cationic dyes and catalytic removal of malachite green. With its facile production process, high removal efficiency, affordable and green nature, and excellent regeneration feasibility, the CS-NC-ZIF-8 aerogel stands as a promising solution for addressing challenges associated with dye-contaminated water treatment.