Preparation, characterization, and application of gallic acid-mediated photodynamic chitosan-nanocellulose-based
Kun Lin1, Yu-Zhang Zhu2, Hua-Wei Ma3
1Key Laboratory of Chemistry and Engineering of Forest Products, State Ethnic Affairs Commission, Guangxi Key Laboratory of Chemistry and Engineering of Forest Products, Guangxi Collaborative Innovation Center for Chemistry and Engineering of Forest Products, Guangxi Minzu University, Nanning 530006, China.
Abstract:
In this study, an active film composed of gallic acid (GA), chitosan (CS), and cellulose nanocrystals (CNC) was prepared using a solution casting method and synergistic photodynamic inactivation (PDI) technology. Characterization of the film showed that the CS-CNC-GA composite film had high transparency and UV-blocking ability. The addition of GA (0.2 %-1.0 %) significantly enhanced the mechanical properties, water resistance, and thermal stability of the film. The tensile strength increased up to 46.30 MPa, and the lowest water vapor permeability was 1.16 × e-12 g/(cm·s·Pa). The PDI-treated CS-CNC-GA1.0 composite film exhibited significantly enhanced antibacterial activity, with inhibition zone diameters of 31.83 mm against Staphylococcus aureus and 21.82 mm against Escherichia coli. The CS-CNC-GA composite film also showed good antioxidant activity. Additionally, the CS-CNC-GA1.0 composite film generated a large amount of singlet oxygen under UV-C light irradiation. It was found that using the CS-CNC-GA1.0 composite film for packaging and storage of oysters at 4 °C effectively delayed the increase in pH, total colony count, and lipid oxidation in oysters. In conclusion, the CS-CNC-GA composite film based on PDI technology has great potential for applications in the preservation of aquatic products.