Experimental Observation of the Fully Ferroelectric-Fully Ferroelastic Effect in Multiferroic Hybrid Perovskites

Since the concept of "multiferroic" was first proposed in 1968, the coupling effect between different ferroic orders has attracted great interest in energy, information, and biomedical fields. However, the fully ferroelectric-fully ferroelastic effect has never been experimentally observed in hybrid perovskites, even though this effect was predicted to exist half a century ago. Realizing such cross-linking effects of polarization vectors and strain tensors has always been a huge challenge because of the complex difference in these two ferroic origins. Here, we report a multiferroic with full ferroelectricity and full ferroelasticity in two-dimensional (2D) hybrid perovskites based on ferroelectrochemistry. The dynamic molecular reorientations endow (cyclohexanemethylaminium)₂PbCl₄ with a desired symmetry change of 4̅2mFmm2 at a Curie temperature of 411.8 K. More strikingly, the switchable evolution of ferroelastic domains was directly observed under the control of either electric or mechanical fields, which is the first experimental observation of a fully ferroelectric-fully ferroelastic effect in hybrid perovskites. This work would provide new insights into understanding the intrinsic cross-linking mechanism between ferroelectricity and ferroelasticity toward the development of multichannel interactive microelectronic devices.