Enhanced Thermoelectric Performance of N-Type PbSe Through Semi-Coherent Nanostructure by AgCuTe Alloying

N-type PbSe thermoelectric materials encounter challenges in improving the power factor due to the single-band structure near the Fermi level, which obstructs typical band convergence. The primary strategy for enhancing the thermoelectric figure of merit (ZT) for n-type PbSe involves reducing lattice thermal conductivity (κ_lat) by introducing various defect structures. However, lattice mismatches resulting from internal defects within the matrix can diminish carrier mobility, thereby affecting electrical transport properties. In this study, n-type AgCuTe-alloyed PbSe systems achieve a peak ZT value of ≈1.5 at 773 K. Transmission electron microscopy reveals nanoprecipitates of Ag₂Te, the room temperature second phase of AgCuTe, within the PbSe matrix. Meanwhile, a unique semi-coherent phase boundary is observed between the PbSe matrix and the Ag₂Te nanoprecipitates. This semi-coherent phase interface effectively scatters low-frequency phonons while minimizing damage to carrier mobility. Additionally, the dynamic doping effect of Cu atoms from the decomposition of AgCuTe within the matrix further optimize the high-temperature thermoelectric performance. Overall, these factors significantly enhance the ZT across the whole temperature range. The ZT value of ≈1.5 indicates high competitiveness compared to the latest reported n-type PbSe materials, suggesting that these findings hold promise for advancing the development of efficient thermoelectric systems.