Chemical and structural transformations of lignin in sesame seed hull during roasting

To investigate the mechanism of lignin degradation during sesame roasting, structural transformations of milled wood lignin (MWL) from sesame seed hull samples roasted at 190-250 °C for 30 min were investigated. The findings revealed that, with increasing temperature, the degradation extent of carbohydrates from lignin carbohydrate complex in the fractions deepened, which reduced total sugar content (from 8.59 % to 0.45 %). Compared to that of the original sesame seed hull lignin (LSSH), the molecular weight of MWL fractions showed a tendency to decline (M_w 4377-2235 Da) with the rise of roasting temperature (210-250 °C). During roasting, lignins in the sesame seed hull underwent degradation and condensation. Due to demethoxylation, the H-type lignin proportion increased from 2.7 % to 26.1 %. Compared to G- and C-type lignin, S-type lignin was more stable. The β-O-4 linkages decreased from 5.8 to 1.2/100 Ar due to CO bond breaking, and β-β linkages from 26.3 to 9.6/100 Ar decreased due to condensation of CC. As the roasting temperature increased, more chemical bonds between lignin structural units were broken, resulting in the generation of more phenolic hydroxyl groups (1.80-2.53 mmol/g). This study helps to elucidate the contribution of lignin degradation during roasting to the oxidative stability of sesame oil.